Three-dimensional printing of temporary crowns with polylactic acid polymer using the fused deposition modeling technique: a case series

Article information

J Yeungnam Med Sci. 2023;40(3):302-307

Publication date (electronic) : 2022 November 4

doi : https://doi.org/10.12701/jyms.2022.00612

Eun-Kyong Kim¹, Eun Young Park², Sohee Kang^,2

¹Department of Dental Hygiene, College of Science and Technology, Kyungpook National University, Sangju, Korea

²Department of Dentistry, Yeungnam University College of Medicine, Daegu, Korea

Corresponding author: Sohee Kang, DDS, PhD Department of Dentistry, Yeungnam University College of Medicine, 170 Hyeonchung-ro, Nam-gu, Daegu 42415, Korea Tel: +82-53-620-3282 • Fax: +82-53-629-1772 • E-mail: kangsh@yu.ac.kr

Received 2022 September 2; Revised 2022 September 14; Accepted 2022 September 22.

Abstract

Introduction

Temporary crowns are a critical part of fixed prosthodontic treatment because they protect the prepared teeth, provide positional stability, and maintain functions, such as mastication and esthetics [1]. Temporary crowns can be fabricated directly on the prepared tooth or indirectly on a model of the prepared tooth [2]. The direct method is convenient but entails significant disadvantages such as irritation to the adjacent tissue and polymer shrinkage [3]. In addition, the chemical odor generated during polymerization causes severe discomfort to patients. The conventional indirect fabrication method can overcome these shortcomings [2], but additional processes, such as impression making and plaster modeling, may be required. If the temporary crown is prepared arbitrarily before tooth preparation, its accuracy is reduced, causing similar problems in the relining process as in the direct method. If the temporary crown is prepared by an indirect method after tooth preparation, the chair time will increase because of the impression and model-making processes.

However, with the recent development of digital dentistry, an indirect temporary prosthesis fabrication method using three-dimensional (3D) printing has been introduced and is being actively developed to overcome the limitations of the conventional indirect method. For fabricating 3D objects from 3D digital data, 3D printing is an additive manufacturing technique. A 3D-printed temporary crown is manufactured through a digital flow process that includes 3D scanning of the prepared tooth, digitalization on a computer, transfer to the 3D printer, and fabrication of the 3D structure [4].

The 3D-printing technologies commonly used for preparing dental polymers include stereolithography apparatus (SLA), digital light processing (DLP), material jetting (MJT), and fused deposition modeling (FDM) [5]. SLA and DLP are currently the most popular technologies in dentistry. Both processes produce 3D structures by the photopolymerization of a liquid photopolymer and can quickly produce high-resolution restorations [6]. MJT is a direct 3D-printing process in which molten droplets of material are ejected onto a heated build platform and bonded; MJT is also accurate and fast, but it is expensive. In the FDM technique, 3D structures are fabricated such that the solid filament material is melted in a nozzle, polymerized while being extruded, and stacked layer by layer. The equipment and materials required for FDM are less expensive and more convenient to use than those required for SLA or DLP. However, although 3D objects printed by FDM have appropriate physical properties, they are not popular in dentistry because they require a long printing time and have low resolution [4].

Interest in the 3D printing of temporary crowns has been increasing, but limited studies have assessed the use of 3D-printing technologies and materials used for manufacturing temporary prostheses. A few studies on 3D printing of temporary crowns have focused on SLA and DLP [7,8]. However, FDM has advantages such as being economical, highly convenient, and producing material with appropriate physical properties. If the shortcomings of the rough surface of the end product and slow working speed are improved, FDM could be successfully used in dental clinics.

Herein, we report our experience with the printability and clinical application of a relatively convenient filamentous polymer (polylactic acid [PLA]; QUVE Co. Ltd., Seoul, Korea), which has been developed and marketed as a temporary restoration material for use in FDM 3D printers (CUBICON Style Plus - A15D; CUBICON Co. Ltd., Seoul, Korea).

Cases

Potential participants were recruited from among patients who visited a dental clinic in Yeungnam University Medical Center from June to August 2022. Five patients were enrolled, and five teeth were scheduled for treatment with a single full-coverage restoration. The teeth were prepared by an experienced dentist, and 3D-printed temporary crowns were luted onto the prepared teeth with Temp-Bond NE (Kerr Dental, Brea, CA, USA) and maintained until the final prosthesis was ready.

After tooth preparation, intraoral scanning of the prepared tooth was performed using a 3D scanner (Medit i500; MEDIT Corp., Seoul, Korea) (Fig. 1). The digital data were then transferred to a NexWay platform (QUVE Co. Ltd.) as an STL file, and the temporary crown was designed by an experienced dental technician using computer-aided design/computer-aided manufacturing (CAD/CAM) software (Exocad GmbH, Darmstadt, Germany) (Fig. 2). Finally, the design was transferred to an FDM 3D printer (CUBICON Style Plus - A15D) installed in the dental clinic and printed into a 3D structure using PLA polymer (Fig. 3).

Fig. 1.

Intraoral scanning after tooth preparation. (A) Three-dimensional scanner (Medit i500; MEDIT Corp., Seoul, Korea). (B) Intraoral scanning image.

Fig. 2.

Crown design using computer-aided design/computer-aided manufacturing (CAD/CAM) software (Exocad GmbH, Darmstadt, Germany). (A) Lateral view. (B) Occlusal view.

Fig. 3.

Fabrication of a three-dimensional (3D)-printed temporary crown using the fused deposition modeling (FDM) method and polylactic acid (PLA) polymer. (A) FDM 3D printer (CUBICON Style Plus - A15D; CUBICON Co. Ltd., Seoul, Korea). (B) Nexway PLA (QUVE Co. Ltd., Seoul, Korea). (C, D) Fabrication of a single temporary crown using PLA. (E) Single temporary crown made with PLA.

5. Case 5

An 80-year-old man complained of pain emanating from tooth #14 when biting, and chewing difficulty over the entire dentition. The maxillary right first premolar was diagnosed with irreversible pulpitis. He experienced prolonged abnormal occlusion due to missing teeth #15, 16, 17, 45, 46, and 47; therefore, the remaining anterior teeth showed severe pathological attrition, and there was no space for the prosthesis in the mandible. Root canal treatment was planned for tooth #14, which was subsequently covered with a surveyed crown so that it could be used as an abutment for removable partial dentures. Owing to the short clinical crown length and low esthetic expectations, a gold crown was planned, and a temporary crown was fabricated with PLA using the FDM method.

The printing process for each crown took approximately 7 minutes. The workplace was not polluted by noise or dust and was kept clean. No failure occurred due to fracture or dislodging of the temporary crown, and no complaints of discomfort, poor esthetics, or surface roughness were reported during the temporary restoration period, which took an average of 7 days (Table 1). Occlusal adjustment was achieved using a denture bur, as would be performed with a temporary, conventional direct resin crown. However, these single provisional crown cases required almost no occlusal adjustment, as few high spots or guide interferences were observed.

Table 1.

Characteristics of the patients and three-dimensional printing of temporary crowns

Discussion

With the recent development of digital equipment and materials in the dental field, the popularity of digital dental technologies has increased [9-11]. The digital process of printing crowns is a novel method that is highly accurate and has low technique sensitivity, allowing dental prostheses to be manufactured by 3D printing, including model-making, without complex lab work [12-14].

Although 3D printing is fast and precise and most printed objects have smooth surface, it is mostly used to produce temporary prostheses. The brittleness, easy deformability, poor weather resistance, and low biocompatibility of 3D-printed objects fabricated using the photo-curing technique limit their performance [15].

Various types of 3D printers and materials are used in the 3D printing of temporary prostheses; however, evidence of their clinical application is still lacking. Therefore, advanced research on materials for the 3D printing of temporary restorations is needed [4]. Convenience, cost, and accuracy are more important factors for temporary crowns than for permanent prostheses.

The equipment and materials involved in SLA are expensive and inconvenient for clinical handling because of the sticky and messy photopolymer used. SLA also produces large amounts of waste material [4,5]. However, the equipment and materials involved in FDM are relatively economical, easy to handle, and possess excellent strength [16].

PLA is one of the most commonly used materials in FDM printers. PLA is biocompatible and nontoxic because it is synthesized from renewable resources, such as sugarcane or cornstarch [17]. In a few in vitro studies, 3D-printed temporary crowns fabricated with PLA using an FDM printer were appropriate in terms of fit and mechanical strength. Molinero-Mourelle et al. [18] reported that the mean marginal fit of PLA provisional crowns was 122.89±26.04 µm, which was clinically acceptable. Crenn et al. [19] reported that PLA temporary crowns had superior flexural strength (115.8±2.11 MPa), hardness (Vickers hardness number of 17.5±0.7), and elastic modulus (3,784±98.9 MPa) compared with those of temporary crowns fabricated with poly(methyl methacrylate), which is an autopolymerizing temporary resin used in the conventional direct method. However, there is a lack of evidence regarding the clinical application of PLA provisional crowns.

Hence, we examined the efficiency of PLA as a temporary crown material fabricated using an FDM dental 3D printer. We used the PLA polymer that was made by blending less than one part polybutylene adipate-co-terephthalate with more than nine parts PLA. All 3D temporary crowns manufactured using this PLA were simply and accurately applied after intraoral scanning.

Both the printer and PLA were easy to handle in the clinic, the workload of the dental staff was reduced owing to digitalization, and contamination of the clinic by volatile liquids was reduced. There were no complaints of patient discomfort and no failures, including fractures and dislodgements, occurred until the final prosthesis was ready. However, PLA products tend to undergo thermal degradation, making high-speed polishing difficult. Therefore, it is important to find ways to reduce the surface roughness of PLA crowns.

The average working time for the 3D printing of temporary crowns is 21±5 minutes, which is shorter than the time taken for the direct method, and similar to the time required for impression taking, enabling the efficient use of chair time.

In the 3D-printing process, after tooth preparation, points that require correction can be checked and corrected immediately on the screen by direct communication between the dental technician and the dentist. Digital data can also be used to fabricate permanent prostheses.

However, our reported cases were limited to single restorations in the posterior region, which is associated with the fact that the accuracy of oral scanning is limited to single-tooth or short-span prostheses. Along with improvements in digital scanning, further research on long-span 3D-printed prostheses should be conducted. Because of the limited surface texture of PLA temporary crowns, their application was limited to the posterior teeth; this limitation should be addressed in future studies to enable the use of 3D-printed crowns for anterior teeth. In addition, assessment of the patients in this study was subjective. Further studies are needed to evaluate PLA 3D-printed crowns using objective data.

Article information Continued